Proses pembentukan senyawa LIB (C2O2)2 dengan variasi suhu sintering.
Telah dilakukan penelitian tentang pembentukan senyawa Lin(CO), atau Lithium bis (oxalato) borate atau LIBOB. LIBOB merupakan kandidat utama pengganti LiPT, yang merupakan elektrolit baterai lithium yang sangat beracun dan berbahaya bagi kesehatan manusia. Lithium bis (oxalato) borate ini dibuat dengan metode metalurgi serbuk dengan mencampurkan bahan baku (produk Merck Germany), yaitu H,C,O, 2H,O, LOH dan H,BO, Mereka dicampur Berdasarkan analisa DTA, kalsinasi dilakukan pada temperatur 120 °C selama 4 jam, kemudian sintering dilakukan dengan rasio mol 02:01:01 sampai homogen. Sebelum kalsinasi dan sintering bahan tersebut dianalisa dengan DIA dengan variasi suhu 230, 240, 245, dan 250 °C selama 6 jam tanpa dialiri gas Nitrogen. Hasilnya dibandingkan dengan LIBOB produk Sigma Aldrich yang cenderung bersenyawa hidrat. Hasil pengamatan menunjukkan bahwa XRD patron LIBOB hasil sintering pada temperatur 240-250 °C 6 jam tanpa dialiri gas Nitrogen, mempunyai kesamaan patron dari LIBOB komersial. Proses pembentukan senyawa LiB(C2O4)2 sangat dipengaruhi oleh temperatur sintering. Serryawa LIB(CO); komersial maupun hasil penelitian ini masih dalam bentuk hidrat atau masih mengandung kristal air, HBO, dan LiHCO sehingga perlu dimurnikan sebelum diaplikasikan dalam baterai sebagai larutan elektrolit untuk mendapatkan hasil yang sempurna.
KATA KUNCI: metalurgi serbuk, sintering, elektrolit, baterai lithium, air kristal, LIBOB
A study concerning the formation of compound LIB(CO); or Lithium bis (oxalato) borate or LIBOB human health. Lithium bis (oxalato) borate was prepared by powder metallurgy method by mixing raw materials LIBOB is a prime candidate replacement LiPF, electrolyte lithium batteries which are very toxic and dangerous to homogeneous. Before calcining and sintering the material in DTA analysis. Based on DTA analysis, calcination was (products Merck Germany), which H2C2O4.2H2O, LiOH and HBO,. They are mixed with a mole ratio of 2:01:01 until carried out at 120°C for 4 hours, then sintering temperature variation performed with 230, 240, 245, and 250 C for 6 hours without Nitrogen gas flowed. The results were compared with LIBOB Sigma Aldrich products that tend to be bound hydrate. The results showed that the patron LIBOB XRD results sintering at temperatures of 240-250°C 6 hours without Nitrogen gas flowed, have in common patron of commercial LIBOB. The process of formation of compound LIB(C2O4)2 is strongly influenced by the sintering temperature. Compound lib (C204), commercial and research is still batteries as an electrolyte solution to get perfect results.
KEYWORDS: powder metallurgy, sintering, electrolyte, lithium battery, crystal water, LIBOB
Ketersediaan
Tidak ada salinan data
Informasi Detil
Judul Seri |
Jurnal Telaah Ilmu Pengetahuan dan Teknologi
|
---|---|
No. Panggil |
Rak Teknologi Telaah Vol. 31 (1) 2013
|
Penerbit | Pusat penelitian Fisika - LIPI : Tangerang., 2013 |
Deskripsi Fisik |
Hal. 39-44, Vol. 31 no. 1 Mei
|
Bahasa |
Indonesia
|
ISBN/ISSN |
0125-9121
|
Klasifikasi |
NONE
|
Tipe Isi |
-
|
Tipe Media |
-
|
---|---|
Tipe Pembawa |
-
|
Edisi |
Vol. 31 No. 1 Mei 2013
|
Subyek | |
Info Detil Spesifik |
-
|
Pernyataan Tanggungjawab |
Titik Lestariningsih, Etty Marty Wigayati, Bambang Prihandoko
|
Versi lain/terkait
Tidak tersedia versi lain